Manganese Mill Liners Manufacturer

When it comes to manganese mill liners, Nanjing JYS Casting is one of the largest austenitic manganese steel cast foundries in China. With over 20 years of cast technology, Our austenitic manganese steel mill liners span life more than other foundries.

The hardness of manganese steel in the solution annealed and water quenched condition is normally around 220 HB. It is possible to strain to harden this material to approximately 500 HB. In order to achieve this high hardness level, the impact loading must be high while the material wearing away from gouging abrasion is limited. It is typical in crushing applications were the main wear mechanism is gouging abrasion that the manganese steel will harden to some intermediate level, typically 350-450 HB.

This material used for grid liners, and generally smaller mills. Its great advantage is that it work hardens under stress, yet the substrate remains tough and can withstand extreme impacting without fracture. Its primary disadvantage is that it spreads with impact, so solid liners begin to squeeze together and become extremely difficult to remove, and can damage a mill shell if the stress is allowed to build up to an extreme level.

Austenitic Manganese Mill Liners Chemical Composition

 Name  Spec Available(%)
C Si Mn Cr Mo Cu P S
High Manganese Liner  (Mn14) 0.9-1.5 0.3-1.0 11-14 0-2.5 0-0.5 ≤0.05 ≤0.06 ≤0.06
Super Manganese Liner (Mn18) 1.0-1.5 0.3-1.0 16-19 0-2.5 0-0.5 ≤0.05 ≤0.06 ≤0.06

 

Austenitic Manganese Mill Liners Mechanical Properties & Microstructure

Name Surface(HB) Ak(J/cm2) Microstructure
High Manganese Liner  (Mn14) ≤240 ≥100 A+C
Super Manganese Liner (Mn18) ≤260 ≥150 A+C
C -Carbide  A- Austenite